Available online 10 November 2023

Valid attritional wear simulation requires a co-efficient of variation ∼10%.

CAD/CAM leucite-reinforced glass-ceramic antagonists can simulate attrition.

Occlusal and buccal polished enamel samples wear at similar rates in vitro.

Attrition results in subsurface damage of human enamel due to mechanical wear.

Investigate attrition simulation using CAD/CAM leucite-reinforced glass-ceramic antagonists on occlusal vs. buccal enamel.

Three dental materials with known wear rates (resin-modified glass-ionomer, micro-filled, and fine particle composites) validated the wear simulator (CAD/CAM glass-ceramic antagonists, 200 cycles, 80 N load, deionised water irrigation, 0.7 mm sliding movement). Following this, human molars were sectioned into paired occlusal and buccal polished samples (n = 8/gp). Exposed 1.5 mm Ø enamel areas were subjected to attritional wear with and without pre-immersion in citric acid (5 min, 0.3%, pH 3.8). Profilometry measured step-height enamel wear and surface microhardness at different depths was calculated using Vickers indentation at 0.1 N and 0.5 N loads.

Dental material wear using the CAD/CAM antagonists showed consistency with previous data: mean (SD) resin-modified glass ionomer material loss of 177.77 (16.89) µm vs. 22.15 (1.30) µm fine particle hybrid composite resin wear vs. 13.63 (1.02) µm micro filled composite resin wear (P < 0.001). The coefficient of variation was less than 10%. Following validation, enamel sample wear was significantly increased when attrition was introduced (P < 0.001) independent of buccal vs. occlusal sample location (P < 0.05). Attrition resulted in occlusal wear of 26.1 ± 4.5 µm vs. buccal 26.3 ± 1.2 µm and attrition/erosion resulted in occlusal wear of 26.05 ± 4.46 µm vs. buccal 25.27 ± 1.16 µm. Whereas erosion-alone resulted in occlusal wear of 1.65 ± 0.13 µm and buccal 1.75 ± 0.03 µm. Microhardness testing at different loads revealed significantly greater hardness reductions in occlusal enamel vs. buccal enamel for 0.1 KgF indentations (P < 0.001) whereas in contrast 0.5 KgF indentations showed no differences.

Wear simulation with CAD/CAM glass ceramic antagonists produced consistent wear in dental materials and human enamel, regardless of enamel surface origin. Lighter (0.1 KgF) hardness testing of occlusal vs. buccal origin revealed damage to the mechanical integrity of the superficial worn enamel.

CAD/CAM

Attrition

Enamel

Ceramic

Dental materials wear

© 2023 The Authors. Published by Elsevier Inc. on behalf of The Academy of Dental Materials.